Ceramic Inserts For Hard Turning

Hard part turning offers improved flexibility better lead times and higher quality.

Ceramic inserts for hard turning.

Use optimized cbn grades for hard part. Applying ceramic cutters is different but it s not alien. The life of cbn inserts typically is more predictable than that of ceramic inserts. For steels softer than approximately 55 hrc use ceramics or cemented carbide inserts.

However the cbn pcbn and ceramic inserts can be expensive especially when compared with the relatively low costs of grinding wheels. Superior heat resistance enables high speed machining aluminium oxide ceramic. But don t let the high cost of inserts scare you off from the hard turning process as the high tooling costs are quickly offset by reductions in processing time and change over time. Kyocera s ceramic inserts are designed to resist oxidation and maintain hardness at elevated temperatures.

Ceramic inserts are recommended for turning of carbon and alloy steels 38 64 rc or rough finish turning of cast iron. Flank wear also commonly appears in hard part turning and typically indicates a need to reduce speeds. With a properly tuned hard turning process these inserts are second only to grinding in terms of holding diameter tolerances. Features of ceramic inserts.

Ceramic is not as tough as cbn and it normally is not used when tolerances are tighter than 0 001 inch. When hard turning with ceramic or cbn inserts crater wear will occur on optimized processes though if it occurs excessively there may be a need to reduce speeds or switch to an insert with a lower cbn content and better wear resistance. Cubic boron nitride cbn grades are the ultimate cutting tool material for hard part turning of case and induction hardened steels.